Novel Ultrafast Lu2O3:Yb Ceramics for Future HEP Applications

Resumen

Inorganic scintillators activated by charge transfer luminescence Yb3+ are considered promising ultrafast material to break the ps timing barrier for future high energy physics applications. Inorganic scintillators in ceramic form are potentially more cost-effective than crystals because of their lower fabrication temperature and no need for aftergrowth mechanical processing. This paper reports an investigation on Lu2O3:Yb and Lu2xY2(1-x)O3:Yb scintillating ceramic samples fabricated by Radiation Monitoring Devices Inc. All samples show X-ray excited luminescence peaked at 370 nm. Ultrafast decay time of 1.1 ns was observed by using a microchannel plate-photomultiplier tube-based test bench at Caltech. Considering its intrinsic high density (9.4 g/cm3), Lu2O3:Yb ceramics are promising for future time of fight application for high energy physics experiments.