41   Artículos

 
en línea
Henryk Kania and Anzelina Marek    
Zn-Al-Mg-Si coatings are an excellent alternative to conventional hot-dip galvanizing coatings. Their high corrosion resistance in corrosive environments containing chlorides and CO2 is well recognized. But sulfur dioxide is also an important stimulator ... ver más
Revista: Applied Sciences    Formato: Electrónico

 
en línea
Christine E. Sanders and Raymond J. Santucci, Jr.    
A rigorous assessment of marine atmospheric corrosion at a controlled NRL test site in Key West Florida was conducted. Certain factors which have been previously implicated in the literature as influencing the corrosion of engineering materials in atmosp... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico

 
en línea
Yanjing Fan, Jianrong Pan, Zhixiao Wu, Bin Li and Zhan Wang    
The durability and safety of steel structures during their life cycle are affected by steel corrosion. Limited test conditions and time hinder the reproduction of actual atmospheric steel corrosion. Most test studies have focused on the effect of pitting... ver más
Revista: Buildings    Formato: Electrónico

 
en línea
Dan Persson, Dominique Thierry and Nathalie LeBozec    
The initial atmospheric corrosion of ZM (ZnAlMg)-coated steel in humid air (85% RH) and humid argon (85% RH) containing 320 ppb SO2 was studied using in situ infrared reflection absorption spectroscopy (IRRAS), FTIR-ATR focal plane array (FPA) imaging an... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico

 
en línea
Abraham Sainz-Rosales, Xóchitl Ocampo-Lazcarro, Azalia Hernández-Pérez, Ana Gabriela González-Gutiérrez, Erika Roxana Larios-Durán, Carlos Ponce de León, Frank C. Walsh, Maximiliano Bárcena-Soto and Norberto Casillas    
Background: Evans?s drop is a classic corrosion experiment that is nearly 100 years old, and it is analogous to other corrosion systems promoted by O2 gradients. The availability of more robust finite element software packages opens the possibility to re... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico

 
en línea
Isabel Rute Fontinha and Elsa Eustáquio    
Anodizing is commonly used for corrosion protection of aluminum and its alloys in the construction industry. The anodic aluminum oxide (AAO) coating has a high ability to prevent the development of extensive pitting corrosion in aluminum substrates, part... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico

 
en línea
Vicki J. Keast    
Even though it is a noble metal, silver will corrode in ambient atmospheres, predominantly by reacting with sulfur-containing gases such as hydrogen sulfide (H2S) and carbonyl sulfide (OCS) to form the silver sulfide (Ag2S) acanthite. Other aspects of th... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico

 
en línea
Qiang Tang, Zhibin Hu, Xiaxia Cui, Zechao Tao and Jau Tang    
An atmospheric pressure microwave plasma source operating on water vapor has many potential applications. To avoid the corrosion of metal electrodes in a traditional water vapor microwave plasma system, we propose a simple water vapor electrodeless micro... ver más
Revista: Applied Sciences    Formato: Electrónico

 
en línea
Bin Sun, Lei Cheng, Chong-Yang Du, Jing-Ke Zhang, Yong-Quan He and Guang-Ming Cao    
The atmospheric corrosion behavior of a hot-rolled strip with four types (I?IV) of oxide scale was investigated using the accelerated wet?dry cycle corrosion test. Corrosion resistance and porosity of oxide scale were studied by potentiometric polarizati... ver más
Revista: Coatings    Formato: Electrónico

 
en línea
Igor A. Chaves, Sean de Prazer, Barbara Jardim do Nascimento and Gregory Flowers    
Not counting domestic dwellings, it has been estimated that in Australia alone, some tens of thousands of masonry buildings and structures have exceeded their design life, with many of these being at risk of partial (or worse) collapse from falling or di... ver más
Revista: Corrosion and Materials Degradation    Formato: Electrónico