Valeria Subbotin?,Oleg S?b?l,Valery Belozerov,Valentin Shnayder,Oleksandr Smyrnov
Pág. 6 - 15
It was determined that in an electrolyte containing 1.75 g/L KOH+1 g/L Na2SiO3+2 g/L NaAlO2, with an increase in current density from 15 A/dm2 to 50 A/dm2, the phase composition of the coating changes. In the three-phase state (a...
ver más
|
|
|
|
|
|
|
|
|
|
|
Valeria Subbotin?,Oleg S?b?l,Valery Belozerov,Alexander Subbotin,Yuliya Smyrnova
Pág. 14 - 23
The effect of electrolysis conditions with different electrolyte compositions on the growth kinetics, phase-structural state, and hardness of coatings obtained by microarc oxidation (MAO) on the D16 aluminum alloy (base ? aluminum, main impurity Cu) was ...
ver más
|
|
|
|
|
|
|
|
|
|
|
Valeria Subbotin?,Oleg S?b?l,Valery Belozerov,Ubeidulla F. Al-Qawabeha,Taha A. Tabaza,Safwan Moh`d Al-Qawabah,Valentin Shnayder
Pág. 6 - 14
The influence of electrolysis conditions at different electrolyte compositions on the phase formation and properties of coatings obtained by microarc oxidation (MAO) on an aluminum alloy AMg6 was studied. For electrolysis, three types of electrolytes wer...
ver más
|
|
|
|
|
|
|
|
|
|
|
Valeria Subbotin?,Ubeidulla F. Al-Qawabeha,Valery Belozerov,Oleg S?b?l,Alexander Subbotin,Taha A. Tabaza,Safwan Moh`d Al-Qawabah
Pág. 6 - 13
Coatings with a thickness of about 100 µm were obtained by microarc oxidation of technically pure aluminum and aluminum alloyed with copper and zinc in an alkaline silicate electrolyte at a current density of ~20 A/dm2. The results of studying ...
ver más
|
|
|
|
|
|