The traditional study on fatigue strength for ship structures usually focuses on high cycle fatigue and ignores low cycle fatigue. However, given the recent trend towards large-scale ship development, the stress and deformation experienced by ship struct...
ver más
|
|
|
|
|
|
|
|
|
|
|
Jingxia Yue, Jiankang Lei, Yordan Garbatov and Ke Yang
Many studies have shown that the linear elastic fracture mechanics (LEFM) method based on the stress intensity factor range (?K) has limitations that cannot be ignored. Due to neglecting the influence of plastic deformation near the crack tip, LEFM shows...
ver más
|
|
|
|
|
|
|
|
|
|
|
Qin Dong, Mengyuan Rong and Geng Xu
The crack closure phenomenon significantly influences low cycle fatigue (LCF) crack growth. The crack closure theory deems that a crack can grow only when the applied load is greater than the fatigue crack opening and closing loads. The revised crack clo...
ver más
|
|
|
|
|
|
|
|
|
|
|
Yulin Wang, Shan Gao, Youchun Xu and Fangyi Li
A numerical model of 84 high-strength concrete-filled square steel tubular columns (HSCFST) with local defects is developed using ABAQUS. The effects of parameters such as crack angle, crack length, impact surface and impact energy on the impact resistan...
ver más
|
|
|
|
|
|
|
|
|
|
|
Chunbo Zhou, Feng Gao, Chengzheng Cai, Wenqi Zheng and Liupeng Huo
To investigate the effect of liquid nitrogen on the granite failure process, the deterioration effect of liquid nitrogen on heated granite was investigated from experimental and theoretical perspectives. The mechanical properties of heated granite (25, 1...
ver más
|
|
|
|
|
|
|
|
|
|
|
Yongmei Zhu, Rujun Li and Jiahao Yang
This study focused on the three-dimensional surface crack growth of a spherical pressure shell. Eight maraging steel 18Ni (250) samples were fabricated and tested, and the fatigue crack growth rate curves were obtained. Considering the influence of plast...
ver más
|
|
|
|
|
|
|
|
|
|
|
Nirpesh Vikram,Raghuvir Kumar
Pág. 1018 - 1031
|
|
|
|
|
|