Laser cladding, a novel surface treatment technology, utilizes a high-energy laser beam to melt diverse alloy compositions and form a specialized alloy-cladding layer on the surface of the substrate to enhance its property. However, it can generate subst...
ver más
|
|
|
|
|
|
|
Haitao Yue, Ning Lv, Chenguang Guo, Jianhua Zhai, Weibing Dai, Jianzhuo Zhang and Guochao Zhao
To determine the optimal process parameters for the preparation of a Co-based alloy cladding layer, the experimental research of laser cladding Co-based alloy was carried out based on the optimal process window and grey relational analysis methods with 4...
ver más
|
|
|
|
|
|
|
Feng Li, Shisong Zheng and Fang Zhou
In this study, AlFeCrMoNi1.8Nb1.5 (at.%) eutectic high-entropy alloy (EHEA) coating was successfully prepared on the surface of M2 high-speed steel (HSS) by wide-laser cladding. The effects of laser defocusing amount, laser power, scanning speed, and pre...
ver más
|
|
|
|
|
|
|
Zhijian Wu, Yang Ding and Xuefeng Peng
We fabricated a core-cladding Ge?Sb?Se glass fiber with a Ge12.5Sb15Se72.5 core and Ge15Sb10Se75 cladding, achieved a supercontinuum spectrum spanning from 2 µm to 9 µm by pumping the Ge?Sb?Se fiber with a core diameter of 11 µm using a femtosecond laser...
ver más
|
|
|
|
|
|
|
Feifei Huang, Erju Liu, Yi Qin, Qingrui Wang, Ying Jin, Lei Wen and Hai Chang
By applying 2205 duplex stainless steel powders to repair and improve carbon steel, multi-pass laser-cladding tests were conducted on Q235 carbon steel surfaces with different laser powers in the range of 1.9~2.5 kW in order to evaluate the performance o...
ver más
|
|
|
|
|
|
|
Kefeng Lu, Jian Zhu, Delin Guo, Minghui Yang, Huajian Sun, Zekun Wang, Xidong Hui and Yongling Wu
Nowadays, high-entropy alloys (HEAs) have become a hot research topic in the field of coating materials. However, HEAs have a large wide range of compositional systems, and the differences in their composition inevitably lead to the significant variation...
ver más
|
|
|
|
|
|
|
Linlin Liu, Yueqi Qiao and Peng Xu
Known as having a stress self-accommodation characteristic, the laser cladding shape memory alloy (SMA) coatings have been widely used in material failure repair. Nevertheless, their further development is greatly limited by their low microhardness (250 ...
ver más
|
|
|
|
|
|
|
Tao Wu, Yunxiang Chen, Bo Lin, Litao Yu, Wanyuan Gui, Jiheng Li, Yuan Wu and Dawen Zeng
Wear and corrosion resistant properties of high entropy alloy coatings (HEAC) on H13 steel are of particular interest for industrial applications. The CoCrFeNi HEA/WC composite coatings (HEACC) developed in this study were successfully prepared by incorp...
ver más
|
|
|
|
|
|
|
Bowen Shi, Xiaokai Mu, Huan Zhan, Linhui Deng, Tao Li and Hongchao Zhang
Almost all of the research on cracks in laser cladding is based, at present, on a horizontal substrate, which cannot be directly applied to prepare high performance coatings, especially high hardness coatings, on tilted substrate. In this work, the influ...
ver más
|
|
|
|
|
|
|
Tiankai Li, Haiyang Long, Changming Qiu, Mingming Wang, Dongdong Li, Zhen Dong and Yongliang Gui
When laser cladding is used to repair parts, the interaction of parameters has a significant influence on equipment performance. In order to explore the process parameters and quality of Ni60PTA coating, the statistical relationship between the process p...