In this work, the Cr3C2-25% NiCr powder was deposited on stainless steel with different combustion pressures and powder feed rates using HVOF technique. The microstructure, porosity, micro-hardness, indentation fracture toughness, adhesion strength, and wear resistance at 500 °C of the coatings were investigated. The results showed that HVOF sprayed Cr3C2-25% NiCr coatings possessed low porosity, high micro-hardness, and enough adhesion strength. The powder feed rate had obvious effect on porosity, micro-hardness and indention fracture toughness of the coatings, and the coating sprayed under the powder feed rate of 33.5 g/min possessed the optimal performance. The wear tests illustrated that the HVOF sprayed Cr3C2-25NiCr coating possessed good wear resistance at the temperature of 500 °C, in which the coating sprayed at the powder feed rate of 33.5 g/min had the best wear resistance due to its dense structure and enough fracture toughness.