Resumen
The tribological properties of the FePSiB amorphous/nanocrystalline coatings with Cr and Nb additions were investigated in reciprocating mode against tungsten carbide friction coupling with different dry sliding conditions. The wear rates of the FePSiB-based coatings increase linearly with the normal load and sliding speed. The coatings with Cr and Nb promote the formation of successive and compact oxide film on friction surface, which decreases significantly wear rate of the coating. Nano-mechanical characterization done to map the correlation between the elastic properties and wear resistance. The main damage mechanisms of the FePSiB-based coatings under dry friction conditions are abrasion wear, delamination failure and oxidation wear.