Resumen
Ion layer gas reaction (ILGAR) method allows for deposition of Cl-containing and Cl-free In2S3 layers from InCl3 and In(OCCH3CHOCCH3)3 precursor salts, respectively. A comparative study was performed to investigate the role of Cl on the diffusion of Cu from CuSCN source layer into ILGAR deposited In2S3 layers. The Cl concentration was varied between 7 and 14 at.% by varying deposition parameters. The activation energies and exponential pre-factors for Cu diffusion in Cl-containing samples were between 0.70 to 0.78 eV and between 6.0 × 10-6 and 3.2 × 10-5 cm2/s. The activation energy in Cl-free ILGAR In2S3 layers was about three times less compared to the Cl-containing In2S3, and the pre-exponential constant six orders of magnitude lower. These values were comparable to those obtained from thermally evaporated In2S3 layers. The residual Cl-occupies S sites in the In2S3 structure leading to non-stoichiometry and hence different diffusion mechanism for Cu compared to stoichiometric Cl-free layers.