Resumen
In this study, the wear mechanisms and tribological performance of uncoated and coated carbide tools were investigated during the turning of super duplex stainless steel (SDSS)?Grade UNS S32750, known commercially as SAF 2507. The tool wear was evaluated throughout the cutting tests and the wear mechanisms were investigated using an Alicona Infinite Focus microscope and a scanning electron microscope (SEM) equipped with energy dispersive spectroscopy (EDS). Tribo-film formation on the worn rake surface of the tool was analyzed using X-ray Photoelectron Spectroscopy (XPS). In addition, tribological performance was evaluated by studying chip characteristics such as thickness, compression ratio, shear angle, and undersurface morphology. Finally, surface integrity of the machined surface was investigated using the Alicona microscope to measure surface roughness and SEM to reveal the surface distortions created during the cutting process, combined with cutting force analyses. The results obtained showed that the predominant wear mechanisms are adhesion and chipping for all tools investigated and that the AlTiN coating system exhibited better performance in all aspects when compared with CVD TiCN + Al2O3 coated cutting insert and uncoated carbide insert; in particular, built-up edge formation was significantly reduced.