Khansaa Dawood Salman, Wisam Abed Kattea Al-Maliki, Falah Alobaid and Bernd Epple
This work aims to define the microstructure and to study the mechanical properties of an Al matrix incorporated with various amounts of Fe2O3 (3, 6, 9, 12 and 15 wt.%) with a constant amount of Ag at 1 wt.%. Al/Fe2O3 + Ag hybrid nano-composite samples ar...
ver más
|
|
|
|
|
|
|
|
|
Haixiao Fang, Hongjian Zhao and Jining He
In this study, Ti/Cu multilayer film was deposited by magnetron sputtering and then nitrided at 800 and 900 °C in N2. The microstructure and wear performance were studied. The deposited Ti/Cu multilayer film mainly consisted of Ti and Cu phases. After ni...
ver más
|
|
|
|
|
|
|
|
|
Feifei Huang, Erju Liu, Yi Qin, Qingrui Wang, Ying Jin, Lei Wen and Hai Chang
By applying 2205 duplex stainless steel powders to repair and improve carbon steel, multi-pass laser-cladding tests were conducted on Q235 carbon steel surfaces with different laser powers in the range of 1.9~2.5 kW in order to evaluate the performance o...
ver más
|
|
|
|
|
|
|
|
|
Fangping Yao, Jinhua Li, Lijin Fang and Zhi Ming
In order to maximize the performance of the nickel-based cladding layer without adding a reinforcing phase, ultrasonic vibrations of different frequencies are assisted in the laser cladding process. The morphology of the cladding layer was analyzed by a ...
ver más
|
|
|
|
|
|
|
|
|
Jihong Li, Longyu Lei, Mingke Du, Zhiqiang Zhang and Min Zhang
Due to the huge difference in thermophysical properties, it is difficult to obtain a defect-free bonding interface between copper and steel. A Cu-Ni-Ti interlayer was added between a TiC-reinforced copper matrix composite coating and Q235 steel in this s...
ver más
|
|
|
|