The aim of the work was to assess the possibility of utilizing the waste generated in the injection molding process for the production of new products based on polyamide 6 reinforced with glass fiber. The manufactured samples were prepared with the addition of 5, 10, 15, and 100 wt.% regrind from the runner system. The impact strength, tensile strength, and hardness of injection products were obtained directly and were assessed after conditioning in distilled water for 24 h. Moreover, the structure of the tested materials was assessed using the FTIR method and their thermal properties using the DSC method. The results of the tests confirm that the addition of regrind up to 15 wt.% to virgin polyamide does not adversely affect its impact strength, tensile strength, and hardness. The water-conditioned materials showed higher values of impact strength but lower values of tensile strength and Young?s modulus at a higher elongation at break. The obtained results are important due to the assumptions of the circular economy and the minimization of the amount of waste and material losses during the injection process.