Resumen
This study was to solve the mandrel demolding problem after curing the composite component with complex structure. In this paper, a reusable thermoplastic mandrel with heating softening characteristics was developed by resin transfer molding (RTM). The glass transition temperature (Tg), surface roughness, and reusability of the mandrel, as well as the shape, surface roughness, thickness uniformity, and internal quality of the formed structure, were tested. The result showed that the Tg of the mandrel was between 80 and 90 °C and the surface roughness was less than Ra 0.5 µm. Additionally, the mandrel can be recycled and can still maintain a good shape after 20 times of deformation. By using this method, the demolding process can be realized by heating and softening the mandrel. The profile error of the formed structure was within 0.5 mm, the surface roughness was less than Ra 0.5 µm, the thickness error was within 0.2 mm, and the average porosity of the upper and lower halves of composite parts was 0.72% and 0.61%. All those data showed that the formed part was in good shape and of good quality. The thermoplastic mandrel can solve the demolding problem of composite materials with complex shapes.