Resumen
Photocatalytic membranes possessing both photocatalytic and solid-liquid separation capabilities were developed. These materials are based on ternary 1% CuO/TiO2@GCN (1:9) embedded on cellulose acetate (CA) via the phase inversion method. The CA membranes containing 0.1, 0.3 and 0.5 wt% of 1% CuO/TiO2@GCN (1:9) (CTG?100, CTG?300 and CTG?500) were fabricated. The deposition of 1% CuO/TiO2@GCN (1:9) onto the CA membranes and the consequential changes in the materials? properties were investigated with various characterization techniques. For instance, PXRD, FTIR, and XPS analysis provided evidence that photocatalytic membranes were formed. Electron microscopy and EDX were then used to visualize the photocatalytic membranes and show that the photocatalyst (1% CuO/TiO2@GCN (1:9)) was well dispersed onto the CA membrane. On the other hand, the properties of the photocatalytic membranes were scrutinized, where it was found that the membranes had a sponge-like morphology and that was significantly less hydrophilic compared to neat CA. The removal of KP in water using CTG?500 exhibited over 94% efficiency, while 38% for neat CA was achieved. Water permeability flux improved with increasing 1% CuO/TiO2@GCN (1:9) and hydrophilicity of the membranes. The electrical energy consumption was calculated and determined to be significantly lower than that of the CA membrane. The CTG?500 membrane after every cycle showed self-cleaning ability after operation in drinking and groundwater.