To improve the properties of recycled aggregate concrete, single and composite impregnation treatments were carried out on recycled coarse aggregates with sodium silicate solution, silane slurry, and polyvinyl alcohol solution. The effects of the three chemical modifiers and different impregnation methods on the apparent density, water absorption, and crushing index of recycled coarse aggregates, as well as the basic properties of recycled aggregate concrete, were investigated. Additionally, the microstructure of the surface of recycled coarse aggregate and the interior of recycled aggregate concrete were analyzed by scanning electron microscopy. The experimental results show that the water absorption of recycled coarse aggregate soaked in polyvinyl alcohol solution decreases most significantly, reaching 64.56%. Only the combination of sodium silicate and silane impregnation produces a positive compounding effect, with a significant increase in the apparent density and a significant reduction in the crushing index of the recycled coarse aggregate. Compared with untreated concrete, the slump, compressive strength, splitting tensile strength, and flexural strength of recycled aggregate concrete prepared by sodium silicate and silane composite impregnation are increased by 9.8%, 26.53%, 21.70%, and 14.72%, respectively. The microstructure analysis shows that the composite impregnation treatment of sodium silicate and silane is most conducive to filling the cracks and holes on the surface of recycled coarse aggregate, which makes the interfacial transition zone of recycled aggregate concrete more compact and the structure more stable.