Resumen
Aimed to evaluate the effect of water solubility on chemical properties and surface structure of bioceramic-based (BC-HiFlow and BC-EndoSeqence) compared with resin-based (Adseal) root canal sealers. Fresh mix was inserted into polyethylene mold (n = 10) and subjected to Vicat needle to evaluate the setting time. The set discs were analyzed by Fourier transform infrared (FTIR) spectroscopy then immersed in deionized water for 1, 7, 14 and 28 days. The solubility%, pH changes, released calcium (Ca2+), phosphate (PO43-) and silicon (Si4+) ions were evaluated after each immersion period. The discs were analyzed by scanning electron microscopy/Energy dispersed X-ray (SEM/EDX) before and after solubility test. Although FTIR detected similar composition of both bioceramic-sealers, BC-EndoSequence determined the prolonged setting times. At the end of solubility test, both bioceramic-sealers exhibited significant greater solubility (>3%), alkaline pH (>11) at p < 0.001. Adseal displayed the significant greatest Ca2+ and PO43- released, while BC-HiFlow displayed the significant greatest Si4+ release (p < 0.001). SEM revealed voids and pores on the surface of all tested sealers with the greatest value on Adseal surface. In conclusion, although both bioceramic-sealers had high solubility, BC-Hiflow complied the ISO standard regarding setting time and least surface micropores better than that of BC-EndoSequence.