Resumen
The study evaluated the effect of elapsed time after mixing on the strength properties of lime and iron ore tailings (IOT) treated black cotton soil (BCS) (an expansive tropical black clay) as road construction material. BCS was treated with 0, 2, 4, 6, and 8% lime and 0, 2, 4, 6, 8, and 10% IOT content by dry weight of soil. Tests carried out include Atterberg limits, compaction, unconfined compressive strength (UCS), California bearing ratio (CBR) (unsoaked condition), and microstructure of specimens. Statistical analysis was done using MINI-TAB software. Results show that the liquid limit (LL) of BCS?lime?IOT mixtures decreased with increase in lime and IOT content. The LL values of all the treated BCS increased between 0 and 1 h elapsed time after mixing. On the other hand, the plastic limit (PL) of BCS decreased with increase in lime and IOT content while the plasticity index (PI) decreased from 27.7 to 22.9% for 0% lime/0% IOT content and from 30.6 to 26.6% for 0% lime/10% IOT content. Maximum dry density (MDD) of BCS increased while optimum moisture content (OMC) decreased with higher IOT content. The natural BCS recorded OMC value of 25.6% decreased to 15.2% for 8% lime/10% IOT treatment. The strength (i.e., UCS and CBR values) increased with increase in lime/IOT contents between 0 and 2 h elapsed time after mixing. Peak values were recorded for 8% lime/8% IOT treatment for all lime content considered. Regression analysis shows a strong relationship between the strength properties and the soil parameters. An optimal 8% lime/8% IOT treatment of BCS for elapsed time after mixing not exceeding 2 h was established and is recommended as sub-base material for low-trafficked roads.