The Damage Threshold of Multilayer Film Induced by Femtosecond and Picosecond Laser Pulses

Yunzhe Wang    
Xiangzheng Cheng    
Junfeng Shao    
Changbin Zheng    
Anmin Chen and Luwei Zhang    

Resumen

Laser-induced damage threshold (LIDT) is an essential factor in measuring the anti-laser damage of optical films. The damage threshold and morphology of the Ta2O5/SiO2 multilayer film prepared by electron beam evaporation were studied by femtosecond (50 fs) and picosecond (30 ps) laser irradiations. The results showed that the LIDT of the film was 1.7 J·cm-2 under the femtosecond laser. The damage morphology developed from surface damage to a clear layered structure, and the outline has become more transparent and regular with an increase in the laser fluence. Under the picosecond laser irradiation, the LIDT of the film was 2.0 J·cm-2. The damage morphology developed from small range to thin film layer separation, and the outline changed from blurry to clear with an increase in laser fluence. Therefore, the LIDT of the film decreased with a decrease in the laser pulse width.

 Artículos similares

       
 
Siyi Li, Guowang Jin and Jiahao Li    
Flooding is one of the most frequently occurring meteorological disasters nowadays, and its occurrence can cause significant socio-economic losses. Aiming at the problem that traditional optical remote sensing makes it difficult to monitor floods, this p... ver más
Revista: Applied Sciences

 
Chunxia Yang, Qianxu Zhang, Jia Guo, Jiawei Wu, Yuan Zheng and Ziwei Ren    
In this paper, the parameters of a prototype runner of an axial flow pump are optimized by using the immersion boundary?lattice Boltzmann numerical method based on a large-eddy simulation (LES-IB-LBM). A fish-friendly axial flow pump with a leading-edge ... ver más
Revista: Applied Sciences

 
James Geisbush and Samuel T. Ariaratnam    
The consequences of failures from large-diameter water pipelines can be severe. Results can include significant property damage, adjacent damage to infrastructure such as roads and bridges resulting in transportation delays or shutdowns, adjacent structu... ver más
Revista: Water

 
Zhongguang Sun, Qinghua Zhang, Jun Zhang, Yi Zhang and Pengfei Wang    
To study the mechanical damage characteristics of rock under the effect of subversion, a series of mechanical experiments, including both uniaxial and triaxial mechanical compression experiments under various levels of water content were performed. In th... ver más
Revista: Applied Sciences

 
Jian-Xiong Gao, Fei Heng, Yi-Ping Yuan and Yuan-Yuan Liu    
Fatigue damage accumulation will not only cause the degradation of material performance but also lead to the growth of effective stress and critical stiffness. However, the existing fatigue reliability models usually ignore the effective stress growth an... ver más
Revista: Aerospace