Analysis of tribological efficiency of movable junctions "polymeric­composite materials ? steel"

Viktor Aulin    
Oleksii Derkach    
Dmytro Makarenko    
Andrii Hrynkiv    
Andrii Pankov    
Andrii Tykhyi    

Resumen

The paper reports an analysis into tribological efficiency of mating parts "polymeric-composite materials ? steel" is carried out. Improperly selected materials produce significant operating costs in terms of tribology. Therefore, selecting the type of polymeric-composite materials to be used in the structures of nodes and machine parts is a task related to substantial improvement of their technical level.The testing of samples made from polymeric-composite materials for relative abrasive resistance when mated with samples made from steel 45 has made it possible to establish that the lowest value for weight wear was demonstrated by material Nylon 66. Among the examined materials, the closest to Nylon 66 in terms of the values for relative abrasive resistance is the material PA-6-210KS that demonstrated the values that are 1.65 times less. During operation of machines, in the presence of abrasive wear, it is advisable to mate the materials "Nylon 66 ? steel 45" and "PA-6-210KS ? steel 45". The results from a tribotechnical study without lubrication at the friction machine SMC-2 for the mating parts "polymeric-composite material ? steel 45" make it possible to establish that the least wear was demonstrated by sample made from the material UPA-6-30, that is 0.00083 g. In terms of wear resistance, the closest to it is a sample from the material PAG/6.6 R196-GF30, which is 6.1 times greater for weight wear. The sample made from steel 45 mated with a sample from the material UPA-6-30 has the lowest value of weight wear, 0.00005 g. At the same time, the lowest value for the friction coefficient is demonstrated by the mated materials "steel 45 ? UPA-6-30", 0.163. The progress of the mating process is achieved fastest, after 20 minutes, when using the material UPA-6-30 at a temperature in the friction zone of 348±2 K.Our research is necessary to substantiate further utilization and selection of polymeric-composite materials for mating parts working under difficult conditions. The current study is of interest to manufacturers of agricultural and quarry machinery and various transport machines.

 Artículos similares

       
 
Sung-Jun Lee, Gang-Min Kim and Chang-Lae Kim    
The purpose of this study is to improve the mechanical durability and surface frictional characteristics of polymer/ceramic-based composite materials. Polydimethylsiloxane (PDMS)/glass bubble (GB) composite specimens are prepared at various weight ratios... ver más
Revista: Coatings

 
Bogdan Warcholinski, Adam Gilewicz, Piotr Myslinski, Ewa Dobruchowska and Dawid Murzynski    
Al?Cr?N coatings were formed at various nitrogen pressures, substrate bias voltages and substrate temperatures using cathodic arc evaporation. The relationship between technological parameters and properties of the coatings was investigated. The phase an... ver más
Revista: Coatings

 
Anatolii Kobets,Viktor Aulin,Oleksii Derkach,Dmytro Makarenko,Andrii Hrynkiv,Dmytro Krutous,Evgeniy Muranov     Pág. 49 - 57
This paper reports a comparative study of the polymeric materials operating in conjugation with steel. In agricultural engineering, a significant role in structural materials belongs to polymer composites. This type of material is characterized by the lo... ver más

 
Oleksii Papeikin,Oleg Safronov,Larysa Bodachivska,Irina Venger     Pág. 54 - 60
The possibility of using the wastes of the oil and fat industry ? phosphatide concentrates as components of lubricating materials was demonstrated in this paper. At the first stage, amidation of phosphatide concentrate from the purification of rapeseed o... ver más

 
Zhitao Fan, Chao Zhi, Lei Wu, Pei Zhang, Chengqiang Feng, Liang Deng, Bingjun Yu and Linmao Qian    
UV/ozone (UVO)-assisted formation of self-assembled monolayer (SAM) of 1H,1H,2H,2H-perfluorodecyltriethoxysilane (PFDS) was prepared on a glass surface. The effect of UVO exposure time on surface roughness and hydrophilicity was investigated through goni... ver más
Revista: Coatings