One of the major barriers limiting the suitability of TiAl intermetallic alloys for use in the demanding aircraft and automotive industries is their susceptibility to degradation as a result of oxidation at temperatures exceeding 760 °C. Paper presents the characteristics of resistance to cyclic oxidation at 950 °C for Ti?45Al?8Nb?0.5(B, C) alloy with and without protective coating obtained as a result of aluminizing using out of pack method. The characteristics of surface condition were determined by scanning electron microscope with EDS system, transmission electron microscope, and X-ray diffractometer. The favorable behavior of the Ti?45Al?8Nb?0.5(B, C) alloy with a protective coating under cyclic oxidation conditions is a result of a higher content of Al2O3 in the microstructure of the scale and the presence of Al and Nb-rich phases at the substrate interface, which probably constitue a barrier for oxidation process. The high temperature oxidation test revealed that aluminide coating was responsible for a remarkable improvement in the oxidation resistance.