Electrodeposition of a Pd-Ni/TiO2 Composite Coating on 316L SS and Its Corrosion Behavior in Hot Sulfuric Acid Solution

Zhiheng Zhang    
Junlei Tang    
Yingying Wang    
Hu Wang    
Bernard Normand and Yu Zuo    

Resumen

Pd-Ni/TiO2 composite coatings were elaborated on 316L stainless steel by an electrodeposition method. The specimens were obtained from an electrolytic bath that contained various contents (5, 10, and 15 g L−1) of nanosized TiO2 particles. X-ray diffraction (XRD) characterization showed that increasing the TiO2 content in the coatings can decrease the crystal grain size. The surface morphology and chemical composition of the composite coatings were modified by the addition of TiO2 particles in the electrolyte, as shown by scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) methods, respectively. The TiO2 content also significantly affected the mechanical and electrochemical properties of the Pd-Ni/TiO2 composite coatings. The microhardness of the Pd-Ni/TiO2 composite coatings can be enhanced by increasing the TiO2 content in the coatings. With the addition of 5 g L−1 TiO2 particles to the electrolyte, the deposited Pd-Ni/TiO2 composite coating presented a remarkably increased corrosion resistance when exposed to a sulfuric acid solution at 60 °C compared with that of the Pd-Ni alloy coating. Nevertheless, the further addition of TiO2 particles into the electrolytic bath did not further improve the corrosion resistance of the composite coating.

 Artículos similares

       
 
Qifeng Li, Zhenbo Qin, Jingyun Chen, Da-Hai Xia, Yida Deng, Yiwen Zhang, Zhong Wu and Wenbin Hu    
Graphene (Gr) has proved its significant role as a reinforcement material in improving the strength of metal matrix composites due to its excellent mechanical properties. In this paper, Gr/Cu composite film with a layered structure was prepared by layeri... ver más
Revista: Coatings

 
Eleni Rosolymou, Stella Spanou, Caterina Zanella, Dimitris S. Tsoukleris, Susanne Köhler, Peter Leisner and Evangelia A. Pavlatou    
Direct current electrodeposited Sn?Ni/TiO2 nanostructured coatings were produced by embedding two different doped types of TiO2 particles within the alloy matrix, a commercially available doped carbon-based and doped N,S-TiO2 particles. The structural ch... ver más
Revista: Coatings

 
Ning Li, Hong Xu, Xinhui Li, Weizeng Chen, Lijuan Zheng and Lirong Lu    
Ni-Mo-ZrO2 composite coatings were produced by pulse electrodeposition technique from alkaline electrolytes containing dispersed ZrO2 nanopowder. The structure, microhardness, corrosion properties and tribological properties of Ni-Mo-ZrO2 composites with... ver más
Revista: Coatings

 
Andrzej Zielinski and Michal Bartmanski    
Coatings deposited under an electric field are applied for the surface modification of biomaterials. This review is aimed to characterize the state-of-art in this area with an emphasis on the advantages and disadvantages of used methods, process determin... ver más
Revista: Coatings

 
Lixia Ying, Zhen Fu, Ke Wu, Chunxi Wu, Tengfei Zhu, Yue Xie and Guixiang Wang    
The aim of this paper is to obtain Cu–Sn composite coatings incorporated with PTFE and TiO2 particles, which have superior antiwear and friction reduction properties. Electrodeposition was carried out in a pyrophosphate electrolyte, and the electro... ver más
Revista: Coatings